ASTM No. | Fe max | ʻO max | N max | C max | H max | Pd | Al | V | Mo | Ni | ʻO ka lōʻihi | 0.2% Ka ikaika o ka hua min | Ikaika U'i Min |
wt% | wt% | wt% | wt% | wt% | wt% | wt% | wt% | wt% | wt% | % | MPa | MPa | |
Papa 1 | 0.2 | 0.18 | 0.03 | 0.1 | 0.015 | 24 | 170 | 240 | |||||
Papa 2 | 0.3 | 0.25 | 0.03 | 0.1 | 0.015 | 20 | 280 | 345 | |||||
Papa 3 | 0.25 | 0.3 | 0.05 | 0.1 | 0.015 | 18 | 380 | 450 | |||||
Papa 4 | 0.5 | 0.4 | 0.05 | 0.1 | 0.015 | 15 | 480 | 550 | |||||
Papa 5 | 0.4 | 0.2 | 0.05 | 0.1 | 0.015 | 5.5- | 10 | 830 | 900 | ||||
Papa 6 | 0.1 | 16 | 780 | 820 | |||||||||
Papa 7 | 0.3 | 0.25 | 0.03 | 0.1 | 0.015 | 0,12- | 20 | 280 | 340 | ||||
Papa 9 | 0.25 | 0.15 | 0.02 | 0.05 | 0.015 | 2,5- | 15 | 550 | 650 | ||||
Papa 11 | 0.2 | 0.18 | 0.03 | 0.1 | 0.015 | 0.12- | 24 | 170 | 240 | ||||
Papa 12 | 0.3 | 0.25 | 0.03 | 0.1 | 0.015 | 0.3 | 0.8 | 25 | 414 | 499 | |||
Papa 13 | 0.5 | ||||||||||||
Papa 14 | 0.5 | ||||||||||||
Papa 15 | 0.5 | ||||||||||||
Papa 16 | 0.04- | 27 | 345 | 485 | |||||||||
Papa 17 | 0.18 | 0.04- | 35 | 206 | 345 | ||||||||
Papa 18 | 0.04- | 3 | 2.5 | 4 | |||||||||
Papa 19 | 3 | 8 | 4 | ||||||||||
Papa 20 | 0.04- | 3 | 8 | 4 | |||||||||
Papa 21 | 3 | 15 | 15 – 8 | 880 | 915 |